Al-Cr-pillared montmorillonite was synthesized by using bentonite and Al-Cr pillaring solutionsas starting materials. The basal spacing and specific surface areas of the materials were significantly increased rela-tive to those of untreated clays. When the Al/Cr molar ratio ( R ) was 0.10, the d (001) value and specific surfacearea of pillared montmorillonite were 1.9194 nm and 165.7 m2 g- 1 , respectively. Thermal stability of the mate-rials was determined using calcined tests and X- ray diffraction (XRD) analysis. The materials formed at differentR(0.05;0.10;0.15;0.25) exhibit a high thermal stability at 300℃ , especially at initial R = 0.10, the basalinterlayer spacing of materials is stabilized at 1.7313 nm after calcined at 500℃ for 2 h. Adsorption behavior ofthe materials was studied by adsorption experiments. The results show that the Al- Cr-pillared montmorillonites ex-hibit much stronger adsorption capacity on Cr6+ in aqueous solution than untreated clays do.
The spin-polarized MS-Xα method is employed to study the electronic structure and the magnetic property of the SmCo5 compound.According to the calculated resul
Twelve samples of Co-Cu/Al2O3 were prepared by impregnating Al2O3 with cobalt salt followed by copper salt or vice versa. The composition of the prepared sample
By using high pure Magnesium (99.9 wt% )as matrix and multi-walled bended carbonnanotubes ( CNTs ) as reinforced phase, carbon nanotubes/magnesium matrix compos
A stochastic model coupled with transient calculations for the distributions of temperature, solute and velocity during the solidification of binary alloy is pr
Ni-ZrO2 nanocomposite coatings with monodispersed ZrO2 nanoparticles were prepared from the composite plating bath containing dispersant under DC electrodeposit
The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@
The temperature dependence of magnetization of intermetallic compounds molecular field theory (MFT)were studied and the results were consistent with the experim
In this paper, the stochastic particle-trajectory model is proposed for simulating the dynamic behavior of circulating fluidized bed (CFB). In our model, the mo
(001)La0.5 Sr0.5MnO3 +δ films on (001)LaA1O3 substrates were prepared by using a RF magnetron sputtering with powder target.At low temperature, the films exhib
The reaction of the mixed rare earth concentrate including monazite ( REPO4 ) and bastnaesite ( REFCO3 )decomposed by CaO and NaCl additives at the temperature