Sol-Gel Preparation of Zn2 SiO4 :Mn Phosphor Layers on Silica Spheres and Their Luminescent Properti

来源 :稀土学报(英文版) | 被引量 : 0次 | 上传用户:aiming6946s
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The synthesis and luminescence properties of Zn2 SiO4: Mn phosphor layers on spherical silica spheres, i.e.,a kind of core-shell complex phosphor, Zn2SiO4: Mn@ SiO2 were described.Firstly, monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS) Si ( OC2H5 ) 4 under base condition ( using NH4 OH as the catalyst).Secondly, the silica spheres were coated with a Zn2 SiO4: Mn phosphor layer by a Pechini solgel process.X-ray diffraction ( XRD), scanning electron microscope ( SEM), energy-dispersive X-ray spectrum ( EDS )and photoluminescence (PL) were employed to characterize the resulting complex phosphor.The results confirm that1000 ℃ annealed sample consists of crystalline Zn2SiO4: Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521 nm corresponding 4T1 (4G) - 6 A1 (6S) transition, and the possible luminescence mechanism is proposed.
其他文献
By theoretical analysis of heat transfer during the "one-step" directional solidification process, the functional relation between the temperature in solid-liqu
The characteristic of the solar energy cell with the rare earth film according to theory of molecular structure was introduced.When sunlight shines, the molecul
Multi-way principal component analysis (MPCA) had been successfully applied to monitoring the batch and semi-batch process in most chemical industry. An improve
The ceramics with cleaning easily up oil-dirty property were prepared by doping enamel slurry with rare earth elements phosphate composite materials, and then t
A novel method capable of sufficient mixing of titanium powder and methane of carbon source was developed in the synthesis of titanium carbide by induction plas
The spin-polarized MS-Xα method is employed to study the electronic structure and the magnetic property of the SmCo5 compound.According to the calculated resul
Twelve samples of Co-Cu/Al2O3 were prepared by impregnating Al2O3 with cobalt salt followed by copper salt or vice versa. The composition of the prepared sample
By using high pure Magnesium (99.9 wt% )as matrix and multi-walled bended carbonnanotubes ( CNTs ) as reinforced phase, carbon nanotubes/magnesium matrix compos
A stochastic model coupled with transient calculations for the distributions of temperature, solute and velocity during the solidification of binary alloy is pr
Ni-ZrO2 nanocomposite coatings with monodispersed ZrO2 nanoparticles were prepared from the composite plating bath containing dispersant under DC electrodeposit